Tungsten High Heavy Alloy Wnife Plate (bar / rod/ sheet/tube/ ring)

Basic Info.

Model NO.	WNiFe WNiCu
Specification	0.1min Thickness*W*L
Trademark	Jiangchi
Origin	China
HS Code	8101990000
Production Capacity	100t/Year

Product Description

High density tungsten alloy WNiCu WNiFe for counterweight
Tungsten high heavy alloy
-Tungsten Nickel Iron Alloy
-Tungsten Nickel Copper Alloy
Production Method
Blending of tungsten powder with other metal powders and a bonding agent, cooling and sieving.
Pressing the blended powder to the required shape (allowing for shrinkage during the final processing), and shaping the green part component.
Pre-sintering the pressed components to remove the bonding agent.
Final sintering in the hydrogen fed furnace to fuse the powder particles together.
Supplied in bar, square, round and rectangle sizes are available in rough oversize, or turned or ground to exact requirements. Components can also be produced to customer drawings.

Tungsten nickel iron/copper(WNiFe&WNiCu) alloy balls/shots
Material: W90NiCu, W90Ni7Fe3, W92NiCu, W92.5NiFe, W95NiFe, W97Ni2Fe1
1) Density of tungsten shot: 17g-18.5g/cm3
2) Available size: Dia: 2.0mm,dia2.25mm,dia2.5mm,dia3.0mm,dia3.5mm,dia4.0mm,dia4.5mm,
dia5.0mm,dia5.5mm,dia6.0mm,dia6.5mm and so on,the biggest size is dia15mm
High density Tungsten based alloy tungsten bearing ball
Tungsten Alloy Density: (17~18.5)
Tungsten Alloy component: W(88-98)% with the addition of nickel and copper or nickel and iron, etc
Tungsten Alloy applications: For making rotors of aircraft wings, shileding materias for radioactive isotope (Cobalt 60), and formaterials of armor piercing bullets and mould, etc.

Class	Nominal tungsten (weight percent)	Density (g/cc)	Hardness ( HRC )(maximum)
1	90	16.85 - 17.25	32
2	92.5	17.15- 17.85	33
3	95	17.75- 18.35	34
4	97	18.25- 18.85	35

Tungsten high heavy alloy
-Tungsten Nickel Iron Alloy
-Tungsten Nickel Copper Alloy

1.Material: W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
2.Density:16.8-18.8g/cm3
3.Size:
rod dia(1.5 -200) x Length300mm Plate: 0.1min Thickness*W*L

4.Property of tungsten alloy

AMST 21014 class 1
90%WNiFe, 90%WNiCu
Density : 17.0
Hardness: 32HRC max
Elongation: 5-20%
AMST 21014 class 2
92.5%WNiFe, 92.5%WNiCu
Density : 17.2
Hardness: 33HRC max
Elongation: 5-15%
AMST 21014 class 3
95%WNiFe, W95NiCu
Density : 18.0
Hardness: 34HRC max
Elongation: 3-10%
AMST 21014 class 4
97.5%WNiFe, W97.5NiCu
Density : 18.85
Hardness: 35HRC max
Elongation: 1-8%

Tungsten Alloys
EFI Grade	EF17	EF175	EF18	EF185
ASTM B 777-07	1	2	3	4
Weight % Tungsten	90	92.5	95	97
Nominal Density GM/CC	17.00	17.50	18.00	18.50
Minimum* Ultimate Tensile Strength UTS (KSI)	110	110	105	100
Minimum* Elongation %	5	5	3	2
Modulus of Elasticity (KSI)	45,000	48,000	50,000	52,000

We also have other tungsten carbide products:Tungsten Carbide ball/tungsten caride shot1. Tungsten nickel iron/copper(WNiFe&WNiCu) alloy balls/shotsMaterial: W95NiCu, W95NiFe, W90Ni7Fe3, W92Ni5Cu3, W92.5NiFe, W97Ni2Fe1, etc.2. Tungsten carbide alloy balls/shotsGrade: YG6 YG6X YG8 YG10 or as customers' requirementsMaterial: WC94% Co6%, WC92% Co8, etcProperty: Good Wear Resistance,High Hardness3. Tungsten shots/balls specification:1) Density of tungsten shot: 17g-18.5g/cm32) Available size:Dia2.0mm, dia2.25mm, dia2.5mm, dia3.0mm, dia3.5mm, dia4.0mm, dia4.5mm, dia5.0mm, dia5.5mm, dia6.0mm, dia6.5mm and dia10mm, etc., and the biggest size is dia15mm.
Tungsten carbide alloy grade:

Grade	Binder (Wt %)	Density (g/cm3)	Hardness (HRA)	TRS (≥N/mm²)
YG6	6	14.8	90.0	1520
YG6X	6	14.9	91.0	1450
YG6A	6	14.9	92.0	1540
YG8	8	14.7	89.5	1750
YG12	12	14.2	88.0	1810
YG15	15	14.0	87.0	2050
YG20	20	13.5	85.5	2450
YG25	25	12.1	84.0	2550